Performance of Water Oxidation by 3D Printed Electrodes Modified by Prussian Blue Analogues

Texto completo
Autor(es):
Priscilla J. Zambiazi [1] ; Amanda T. N. de Moraes [2] ; Rodrigo R. Kogachi [3] ; Gabriel O. Aparecido [4] ; André L. B. Formiga [5] ; Juliano A. Bonacin [6]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Universidade Estadual de Campinas. Instituto de Química - Brasil
[2] Universidade Estadual de Campinas. Instituto de Química - Brasil
[3] Universidade Estadual de Campinas. Instituto de Química - Brasil
[4] Universidade Estadual de Campinas. Instituto de Química - Brasil
[5] Universidade Estadual de Campinas. Instituto de Química - Brasil
[6] Universidade Estadual de Campinas. Instituto de Química - Brasil
Número total de Afiliações: 6
Tipo de documento: Artigo Científico
Fonte: Journal of the Brazilian Chemical Society; v. 31, n. 11, p. 2307-2318, 2020-10-30.
Resumo

The water oxidation is the limiting step in the water-splitting process. Given this scenario, the development of new catalysts is essential in this field. The emergent demand is the use of Earth-abundant elements and catalysts with high performance under mild conditions. Because of this, catalysts such as Prussian Blue analogues (PBA) have been receiving a lot of attention in recent years. In addition, working under neutral conditions allows us to take advantage of the modification of conductive polymeric 3D printed electrodes (3DPE) with Prussian Blue. Thus, we described in this work the development of the polymeric 3D printed electrodes modified by cobalt-Prussian Blue and their performance in the water oxidation process. The 3D printed electrodes modified with Co3[Co(CN)6]2 (Co-Co PBA) have a Tafel slope of 343 mV dec−1 while those modified with Co3[Fe(CN)6]2 (Co-Fe PBA) have a Tafel slope of 378 mV dec−1. This means that both catalysts have the same mechanism for the water oxidation process. On the other hand, the overpotential of Co-Co PBA in 3DPE is lower than the value observed by Co-Fe PBA in 3DPE suggesting the best electrocatalytic activity for Co-Co PBA catalyst. (AU)

Processo FAPESP: 13/22127-2 - Desenvolvimento de novos materiais estratégicos para dispositivos analíticos integrados
Beneficiário:Lauro Tatsuo Kubota
Modalidade de apoio: Auxílio à Pesquisa - Temático
Processo FAPESP: 17/23960-0 - Estudo de mecanismo de oxidação de água por catalisadores operando em pH=7 e sua incorporação em eletrodos impressos em 3D
Beneficiário:Juliano Alves Bonacin
Modalidade de apoio: Auxílio à Pesquisa - Regular